High quality and large capacity 1000T/M anodizing production line
一.Production Description
1.Anodizing creates a protective oxide layer on the aluminum surface, making it highly resistant to corrosion from moisture, chemicals, and other environmental factors.
2.The anodized layer is much harder and more scratch-resistant than regular aluminum, improving the lifespan and performance of components in high-wear applications like automotive parts, cookware, and outdoor gear.
3.Anodizing allows for a wide range of color options and finishes, from matte to glossy, enabling designers to tailor the aesthetic for various consumer and industrial products.
二. Design Condition
| 1 | Alloy | Aluminium 6061 to 6063 or others |
| 2 | Anodizing film thinkness | 10~ 12µm micron |
| 3 | Average coverage area | 350m²/T (ton) |
| 4 | Max aluminium profile length | 6500mm |
| 5 | Extrusion ratio | 2.5kg/m² |
| 6 | Working hour/m | 300d/m x 20h/d = 600h/m |
| 7 | Racking system | Three fixtures /rack |
| 8 | Racking operation | Manual |
| 9 | Equipment Usage Rate | 0.9 |
| 10 | Power supply | AC 3phase 380v 50hz |
| 11 | Control Power | AC220V 50Hz |
| 12 | Water supply | 2kg/cm²·G |
| 13 | Hot steam | 6kg/cm²·G |
| 14 | Compressor air | 6kg/cm²·G |
三.Process Tank
| 1 | Degreasing 【Free sulfuric acid 180±30 g/l】 | 1 Tank |
| 2 | Alkaline Etching【Free alkali 40-60g/l,Al3+ 30-120g/】 | 2 Tanks |
| 3 | Neutralization 【Free sulfuric acid180±20g/l】 | 1 Tank |
| 4 | Anodising 【Free sulfuric acid 140-180g/l,Al3+≤20g/l】 | 5 Tanks |
| 5 | Colouring 【stannous sulfate 3-8g/l,Free sulfuric acid 15-25g/l,PH 0.8-1.2】 | 2 Tanks |
| 6 | Medium Temperature Sealing【PH 5-6.5,Nickel ion0.8-1.3g/l,Fluorion0.3-0.7 g/l】 | 3 Tank |
四. Treatment Process:
- Degreasing
(1) 6jig(rack)/ tank x 1 tank=6jig(rack)
(2) treatment time: 2-5min - Alkaline Etching
(1) 6jig(rack) / tank x 2 tank=12jig(rack)
(2) treatment time: 3-15min - Neutralization
(1) 6jig(rack) / tank x 1 tank=6jig(rack)
(2) treatment time: 1-5min - Anodizing
(1) 3 jig(rack)/tank x 5tanks = 15jig(rack)
(2) Current density: 130A/m²
(3) Process time: 30min
(4) Unprocess time: 10min
(5) Total time 30+10=40min
(6) Average anodizing layer : 0.36*1.3*30*0.77 =10.81um
- Colour 1
1) Clour process: Mix Salts
2) Quantity:2 jig(rack)/tank x 1tanks = 2jig(rack)
3) Current density: 70A
4) Process time: 2-8min
6. Sealing
1) Sealing menthod: Sealing at Medium or Normal Temperature
2) Quantity:6jig(rack)/tank x 1 tank
3) Process time 10-15min
五. Design Parameter and Setting
1. Anodizing treatment area:
1) Each anodizing process tank need 40min ,where total jig(rack)/year:
( 2rack x 5 tank x 60min/h) ÷40min x600 hour =9000jig(rack)
2) Design 50m²/jig(rack) . Where every tank is 100m²
3) Area treatment/year : 9000jig(rack)x 50m² /jig =450000m²
2. Anodizing treatment weight:
Monthly output : 450000m²÷350m²/T*0.9=1157.1T≧1000T
3. Power consumption:
1) Anodising Tank:100m²/tank* 130A/ m²÷0.9=14444A/tank
Power Rectifier : 15000A =5unit
2) Clouring tank: 100㎡/tank×70A/m²÷0.9 = 7777A/tank
Colour Rectifier : 8000A =2 unit
六. Process Chat
| Discription for Un |
| 1 | De | Degreasing |
| 2 | Rs | Rinsing |
| 3 | HW Rs | Hot Water Rinsing |
| 4 | AE | Alkaline Etching |
| 5 | Ne | Neutralization |
| 6 | An | Anodizing |
| 7 | Cl | Coloring |
| 8 | Sl | Sealing |
| 9 | MU | Material Unloading |
| 10 | Pc | Packing |